PRL TPSF-G10
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iQH5RH_PRL-TPSF-G10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TPSF-G10 is a Polybutylene Terephthalate (PBT) product filled with 10% glass fiber. It can be processed by foam processing and is available in North America. Typical application: Foam. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.0 to 18 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 72.4 | MPa | |
| Break, 3.18 mm | 72.4 | MPa | |
| Flexural Modulus (3.18 mm) | 2960 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 103 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 53 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 138 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 121 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 249 to 260 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS BT231 - 8229 | AD majoris | PP, Unspecified | MAJORIS |
| LUVOCOM® 80-8495-2 | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| KOPA® KN333G30 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| Sylvin 9604-80 Purple 8460 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® AKV 50 H3.0 000000 | LANXESS GmbH | Nylon 66 | Durethan® |