Retpol® PDR 7413/6 UV3 7A13
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iQ5FZN_Retpol-PDR-7413-6-UV3-7A13.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epalex PDR 7413/6 UV3 7A13 is a thermoplastic rubber modified mineral filled polypropylene compound. It is a very high flow injection moulding grade developed for high impact strength and high rigidity at high ambient temperatures, low SG and moderate to high shrinkage. It has been stabilized for continuous outdoor exposure. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.938 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.90 to 1.2 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 52 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 66 | ||
| Shore D, 15 sec, 3.00 mm | 57 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 18.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 470 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 1080 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.00 mm | 90 | J/m | |
| 0°C, 3.00 mm | 440 | J/m | |
| 23°C, 3.00 mm | 560 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 103 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 200 to 260 | °C | |
| Mold Temperature | 20.0 to 60.0 | °C | |
| Injection Rate | Moderate-Fast |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tenite™ Butyrate 530A3720016 Clear, Trsp | Eastman Chemical Company | CAB | Tenite™ Butyrate |
| Wellamid® MR1873-EPBK1 | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| TUFNYL® SST 35 BROWN | SRF Ltd. | Nylon 6 | TUFNYL® |
| 3M™ Dyneon™ PTFE Compound TF 3105 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Sumiliteresin® PR-50869B | SBHPP | Phenolic | Sumiliteresin® |