LNP™ VERTON™ RV00CEXS compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ VERTON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iQ3zze_LNP-VERTON-RV00CEXS-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP VERTON RV00CEXS is a compound based on Nylon 66 resin containing 60% Long Glass Fiber. Added features of this grade include: Easy Molding, Structural. Also known as: LNP* VERTON* Compound RF-700-12 EM Product reorder name: RV00CEXS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.72 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.30 to 0.50 | % | |
| Across Flow : 24 hr | 0.70 to 0.90 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.53 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.67 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 22100 | MPa | ASTM D638 |
| -- | 21900 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 254 | MPa | ASTM D638 |
| Break | 264 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 1.6 | % | ASTM D638 |
| Break | 1.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 18100 | MPa | ASTM D790 |
| -- 5 | 18700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 404 | MPa | ISO 178 |
| Yield, 50.0 mm Span 6 | 404 | MPa | ASTM D790 |
| Break, 50.0 mm Span 7 | 403 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 410 | J/m | ASTM D256 |
| 23°C 8 | 38 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 1200 | J/m | ASTM D4812 |
| 23°C 9 | 62 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 13.6 | J | ASTM D3763 |
| -- | 9.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 252 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 253 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 248 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 247 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 282 to 293 | °C | |
| Middle Temperature | 288 to 299 | °C | |
| Front Temperature | 288 to 299 | °C | |
| Processing (Melt) Temp | 288 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech P240 | Shanghai Suptech Engineering Plastics Co. Ltd. | PP, Unspecified | Sup-tech |
| Unipren® Elastomers A3 NTLA010 45A UP301 | Petropol Industry and Trade of Polymers LTDA | SEBS | Unipren® Elastomers |
| XYRON™ L544V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| Iupilon® HL-7001 | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Plaslube® PPA CF30 TL10 | Techmer Engineered Solutions | PPA | Plaslube® |