ENVIRON® ENV39-NC510
| Category: | PC+PBT , Polycarbonate + PBT |
| Manufacturer: | ENVIROPLAS®, Inc. |
| Trademark: | ENVIRON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iPaII0_ENVIRON-ENV39-NC510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, 30% Fiberglass Reinforced, Flame Retardant, Impact-Modified for Improved Toughness and Ductility, RoHS Compliant NC510 = To Be Assigned 5 Digit Number Indicating Natural, Black, or Custom Color. The ENV39 Series Products Are Available With Mold Release and/or UV Stabilizer. Contact Enviroplas Regarding UL Recognized Versions Of This Product. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.58 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.30 to 0.60 | % | ASTM D955 |
| Ash Content | 30 | % | ASTM D5630 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.0 | % | ASTM D638 |
| Flexural Modulus | 6650 | MPa | ASTM D790 |
| Flexural Strength | 162 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 157 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | Internal Method | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 249 to 271 | °C | |
| Middle Temperature | 254 to 277 | °C | |
| Front Temperature | 260 to 282 | °C | |
| Nozzle Temperature | 254 to 277 | °C | |
| Mold Temperature | 65.6 to 87.8 | °C | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 50 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ranger PBT PBT-MFC-G0 | Beijing Ranger Chemical Co., Ltd. | PBT | Ranger PBT |
| Diakon® CMH454 | Lucite International Inc. | Acrylic (PMMA) | Diakon® |
| Fluon® PTFE PB3360T | Asahi Glass Co., Ltd. | PTFE | Fluon® |
| ICORENE® 9402 | ICO Polymers EMEA, A Division of A. Schulman | TPE | ICORENE® |
| Lupox® SG3180S | LG Chem Ltd. | PBT+PET | Lupox® |