Shuang-Bang CD-1060S
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | Shuang-Bang Industrial Corp. |
| Trademark: | Shuang-Bang |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iNGqsB_Shuang-Bang-CD-1060S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
One component PU Resins PU membrane is produced by coating the resin on substrate and drying it to vaporize the solvent adequately. The membrane gives soft hand-feel and dry surface, and offers waterproof and windproof properties. Using one component type PU resin alone with adequate crosslinker for yarn fixation, following by drying process to vaporize solvent adequately, could form high yarn-bonding membrane. Shoes, leather bag, ready-make clothes Blocking resistance, high water resistance, good hand-feel Surface modifier for high moisture-permeability fabrics. Could increase water pressure without reducing moisture-permeability. Dry hand-feel. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Solvents | DMF/MEK/TOL |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | Off White | ||
| Solids Content | 29 to 31 | % | |
| Viscosity (25°C) | 15 to 30 | Pa·s |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Tensile Modulus (100% Secant) | 3.43 to 5.39 | MPa | |
| Tensile Strength | > 11.8 | MPa | |
| Tensile Elongation at Break | > 400 | % |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom SC1F-4009U | Spartech Polycom | ABS | Spartech |
| TEREZ PA/PP 7810/1 HI | TER HELL PLASTIC GMBH | Nylon 6+PP | TEREZ PA/PP |
| Caltex PP MT64WS | GS Caltex | PP, Unspecified | Caltex PP |
| Fainplast PVC PK 5510 | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Hifax CA 1110 G4 C11306 | LyondellBasell Industries | PP Copolymer | Hifax |