VITAMIDE® BS10BK6573
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iNBr5Z_VITAMIDE-BS10BK6573.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| VITAMIDE® BS10BK6573 is a Polyamide 6 (Nylon 6) product. It is available in Europe. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792, ISO 1183 |
| Water Absorption (23°C, 24 hr) | 2.6 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | |||
| Yield | 75.0 | MPa | ISO 527-2 |
| -- | 75.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 35 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2800 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 5.00 | kJ/m² | |
| Charpy Unnotched Impact Strength 2 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 | |
| Notched Izod Impact Strength | 5.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 195 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648, ISO 75-2/A |
| Peak Melting Temperature | 218 | °C | ASTM D2117, ISO 1218 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 13 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 600 | V | IEC 60112 |
| -- | 600 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-2 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2660 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| SEQUEL® 2326 | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| VITAMIDE® BG35BK6357 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| EGYPTENE HD 5403 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| Karina IVORY PVC COMPOUND 809D35/1-C-AC-AS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |