| 20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.70 | % | |
| Flow | 0.30 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 2.00 mm | 0.78 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.26 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.9 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 6500 | MPa | |
| 1000 hr | 4800 | MPa | |
| Flexural Modulus | 6300 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 7.5 | kJ/m² | |
| 23°C | 9.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 43 | kJ/m² | |
| 23°C | 60 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 8.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -30°C | 50 | kJ/m² | |
| 23°C | 50 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 160 | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 110 | °C | ISO 11357-2 |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| Melting Temperature 2 | 225 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 3.0E-5 | cm/cm/°C | |
| Transverse | 1.0E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Electric Strength | IEC 60243-1 | ||
| -- | 35 | kV/mm | |
| 1.00 mm 3 | 35 | kV/mm | |
| 2.00 mm 4 | 20 | kV/mm | |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.40 | ||
| Dissipation Factor | ASTM D150, IEC 60250 | ||
| 100 Hz | 3.0E-3 | ||
| 1 MHz | 0.018 | ||
| Comparative Tracking Index | 550 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification (1.50 mm) | HB | IEC 60695-11-10, -20 | |
| Oxygen Index | 19 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.19 | g/cm³ | |
| Specific Heat Capacity of Melt | 1850 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.25 | W/m/K |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Odor | 3.5 | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| 3 . | Short Time |
| 4 . | 20 sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP ESD C 2800 B-45A Black | RTP Company | TPO (POE) | RTP |
| RAMSTER PE304G3 | Polyram Ram-On Industries | PET | RAMSTER |
| TOTAL Polypropylene PPC 4624WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| KMI PP KM-0283HB | KMI Group, Inc. | PP Impact Copolymer | KMI PP |
| ALTECH® PA6 A 2050/720 GF50 UV | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |