Flexathene® TP4120BK
| Category: | Polyolefin, Unspecified , Polyolefin |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Flexathene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iIvgUX_Flexathene-TP4120BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FLEXATHENE TP 4120-BK is a high flow injection molding grade thermoplastic olefin (TPO) formulated for thin wall paintable automotive applications. TP 4120-BK has an excellent balance of stiffness, impact resistance, dimensional stability and processability and has been specially formulated to meet GMP.E/P.133. This resin is pre-colored black, but is available in other colors as well as weatherable and UV paintable versions to meet GMP.E/P.134. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.959 | g/cm³ | ISO 1183/A, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 26 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg 1 | 26 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| 121°C, 1 hr | 0.73 to 0.88 | % | |
| 48 hr | 0.53 to 0.68 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1380 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield 2 | 18.9 | MPa | ASTM D638 |
| Yield | 18.9 | MPa | ISO 527-2 |
| Tensile Elongation (Yield) | 8.2 | % | ASTM D638 |
| Flexural Modulus - Tangent | |||
| -- 3 | 1050 | MPa | ASTM D790B |
| -- | 1050 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -18°C | 53 | J/m | |
| 23°C | No Break | ||
| Unnotched Izod Impact (-18°C) | No Break | ASTM D256 | |
| Instrumented Dart Impact 4 | ASTM D3763 | ||
| -30°C, Energy to Peak Load | 24.0 | J | |
| 23°C, Energy to Peak Load | 18.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| CLTE - Flow | 5.4E-5 | cm/cm/°C | ASTM E831 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 204 to 232 | °C |
| Note Message | |
|---|---|
| 1 . | Procedure A |
| 2 . | 13 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.20 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Arnite® TV4 460 KL | DSM Engineering Plastics | PBT+PET | Arnite® |
| Geon™ Vinyl Rigid Extrusion L0676 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| EPLAMID 6 GFT 20 NC | EPSAN Plastik SAN. ve TiC. A.S. | Nylon 6 | EPLAMID 6 |
| Hostacom G3 N01 L | LyondellBasell Industries | PP Homopolymer | Hostacom |
| OnFlex™ BIO 5370A-E0004 | PolyOne Corporation | TPE | OnFlex™ BIO |