Solef® 21510
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Solef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iHWhN5_Solef-21510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Solef® 21510 PVDF copolymer has medium viscosity and is suitable for extrusion and for solution processing in lithium batteries applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 to 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 3.0 to 9.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 360 to 480 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 15.0 to 18.0 | MPa | |
| Break, 23°C, 2.00 mm | 20.0 to 40.0 | MPa | |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00 mm | 12 to 15 | % | |
| Break, 23°C, 2.00 mm | 600 to 750 | % |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
| Melting Temperature | 130 to 136 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 89.0 to 93.0 | °C | ASTM D3418 |
| Crystallization Heat | 20.0 to 24.0 | J/g | ASTM D3417 |
| Heat of Fusion | 20.0 to 24.0 | J/g | ASTM D3417 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Note Message | |
|---|---|
| 1 . | Type IV, 1.0 mm/min |
| 2 . | Type IV, 50 mm/min |
| 3 . | Type IV, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ GV-819.G001-8065 | PolyOne Corporation | PP, Unspecified | Maxxam™ |
| TAROMID A 280 H G6 DX0 TR1 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Bynel® 3861 | DuPont Packaging & Industrial Polymers | EVA | Bynel® |
| ELASTOSIL® E 4 | Wacker Chemie AG | Silicone | ELASTOSIL® E |
| ESPOLEX 901 | Sumitomo Chemical America, Inc. | TPO (POE) | ESPOLEX |