Lusep® GP4600
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lusep® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iHBAVH_Lusep-GP4600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lusep® GP4600 is a Polyphenylene Sulfide (PPS) material filled with 60% glass\mineral. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Primary attribute of Lusep® GP4600: Flame Rated. Typical application of Lusep® GP4600: Engineering/Industrial Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.89 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.10 to 0.20 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break, 3.20 mm) | 118 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 1.0 to 2.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 16900 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 177 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | > 250 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.750 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 280 to 300 | °C | |
| Middle Temperature | 290 to 310 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 310 to 330 | °C | |
| Processing (Melt) Temp | 300 to 330 | °C | |
| Mold Temperature | 120 to 150 | °C | |
| Screw Speed | < 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Zythane® 9026V | Alliance Polymers & Services | TPU, Unspecified | Zythane® |
| Formolene® 6600A | Formosa Plastics Corporation, U.S.A. | PP Impact Copolymer | Formolene® |
| LARIPUR® LPR 8520 | COIM S.p.A. | TPU-Polyester | LARIPUR® |
| INEOS LDPE 28H430 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| Karina IVORY PVC COMPOUND 105905-35/ 1-BY-IS-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |