Order Products : sales@su-jiao.com
Kepamid® 2340GM8
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iGhxZw_Kepamid-2340GM8.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
KEPAMID 2340GM8 is a 40% glass fiber/mineral reinforced polyamide-66. It exhibits good mechanical and thermal properties and low warpage. It is applicable to low warpage applications of automotive, electrical, electronic, and industrial parts. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (275°C/2.16 kg) | 16 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 147 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 2.5 | % | ASTM D638 |
| Flexural Modulus (23°C) | 9410 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 235 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 69 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 255 | °C | |
| 1.8 MPa, Unannealed | 235 | °C | |
| Melting Temperature | 260 | °C | DSC |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (0.800 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Hopper Temperature | 260 to 300 | °C | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 260 to 300 | °C | |
| Front Temperature | 260 to 300 | °C | |
| Nozzle Temperature | 260 to 300 | °C | |
| Mold Temperature | 40.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL TP-GFMF3 | Polymer Resources Ltd. | PBT | PRL |
| Sinpolene MBW1712 | Teknor Apex Asia Pacific PTE. LTD. | PE, Unspecified | Sinpolene |
| SLOVAMID® 6 GF 20 T 10 FRG 5 | Plastcom | Nylon, Unspecified | SLOVAMID® 6 |
| NILENE® E12 | Taro Plast S.p.A. | PP Copolymer | NILENE® |
| Fiberfil® J-60/20/TT/FD WT8381 | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |