Category: | EMAA , Ethylene Methacrylic Acid |
Manufacturer: | DuPont Packaging & Industrial Polymers |
Trademark: | Nucrel® |
Fillers: | - |
Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
Delivery Terms | FOB, CIF, DAP, DAT, DDP |
PDF: | iFL4xe_Nucrel-0407HS.pdf ![]() |
PRICE: | Order Products email sales@su-jiao.com |
Message |
---|
Nucrel® 0407HS is a copolymer of ethylene and methacrylic acid made with nominally 4 wt% methacrylic acid. It is available for use in conventional extrusion coating, coextrusion coating and extrusion laminating equipment designed to process polyethylene resins. |
General Information | |
---|---|
Features |
|
Uses |
|
Agency Ratings |
|
Processing Method |
|
Physical | Nominal Value | Unit | Test Method |
---|---|---|---|
Specific Gravity | 0.930 | g/cm³ | ASTM D792, ISO 1183 |
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238, ISO 1133 |
Methacrylic Acid Content | 4.0 | wt% |
Thermal | Nominal Value | Unit | Test Method |
---|---|---|---|
Freezing Point | |||
-- | 85 | °C | ISO 3146 |
-- | 85 | °C | ASTM D3418 |
Vicat Softening Temperature | 90.0 | °C | ASTM D1525, ISO 306 |
Peak Melting Temperature | 110 | °C | ASTM D3418, ISO 3146 |
Extrusion | Nominal Value | Unit | |
---|---|---|---|
Cylinder Zone 1 Temp. | 185 | °C | |
Cylinder Zone 2 Temp. | 235 | °C | |
Cylinder Zone 3 Temp. | 285 | °C | |
Cylinder Zone 4 Temp. | 310 | °C | |
Cylinder Zone 5 Temp. | 310 | °C | |
Adapter Temperature | 310 | °C | |
Melt Temperature | 260 to 310 | °C | |
Die Temperature | 310 | °C |
Resin Grade | Manufacturer | Category | Trademark |
---|---|---|---|
Xuchuan XCW-8425DH | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
alphalon™ E 36 L | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
Geon™ Vinyl Flexible R296CM | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
Globalene® 7633U | Lee Chang Yung Chemical Industry Corp. | PP Impact Copolymer | Globalene® |
Karina COMP. PVC GRAY -E 680D18/665-B-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Flexible | Karina |