Chemlon® 66GF6
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iClYgK_Chemlon-66GF6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 66GF6 is a reinforced nylon 66 containing 30% glass fiber, which can provide good mechanical properties as well as surface finish and fluidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.38 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | 0.30 - 0.60 | -- | % | Internal method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.50 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 155 | 110 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.0 | 10 | % | ISO 527-2 |
| Flexural Modulus | 7500 | 4600 | MPa | ISO 178 |
| Flexural Stress | ISO 178 | |||
| -- 2 | 200 | -- | MPa | ISO 178 |
| -- 3 | -- | 100 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | 8.0 | 20 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 48 kJ/m² | No Break | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | > 240 | 240 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 240 | 230 | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | 1.0E+12 | ohms·cm | IEC 60093 |
| Dielectric Strength (3.00 mm) | 16 | 10 | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.70 | 4.20 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 0.010 | 0.040 | IEC 60250 | |
| Comparative Tracking Index | 600 | 500 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (Teknor Apex result) | HB | HB | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 270 - 290 | °C | |
| Middle Temperature | 270 - 290 | °C | |
| Front Temperature | 270 - 290 | °C | |
| Processing (Melt) Temp | < 300 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 200 | rpm |
| Injection instructions |
|---|
| 如果材料在空气中暴露的时间不超过3小时，则无需干燥。背压：低注射压力：高 |
| Note Message | |
|---|---|
| 1 . | Mould shrinkage is significantly influenced by many factors including wall thickness, gating, component shape and moulding conditions.The range values stated were determined from specimen bar mouldings of 1.5mm to 4mm wall thickness. They are provided as a guide for comparison purposes only and no guarantee should be inferred from their inclusion. (Specimens measured in the dry state, 24 hours after moulding). |
| 2 . | At Break |
| 3 . | At Yield |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DAI-EL™ G-717 | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Halene P M340 | Haldia Petrochemicals Ltd. | PP Impact Copolymer | Halene P |
| Karina FUM\u00C9 MBATCH (SP31452) -E 27/ 8-GIN | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Sylvin 3270-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| NORYL GTX™ GTX918W resin | SABIC Innovative Plastics | PPE+PS+Nylon | NORYL GTX™ |