Generic TPE
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | iANtpM_Generic-TPE.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic TPE This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.863 - 1.26 | g/cm³ | ASTM D792 |
| 23°C | 0.828 - 1.21 | g/cm³ | ISO 1183 |
| -- | 0.866 - 0.903 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 0.010 - 13 | g/10 min | ASTM D1238 |
| 230°C/2.16 kg | 0.20 - 18 | g/10 min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.86 - 2.9 | % | ASTM D955 |
| Transverse flow : 23°C | 1.1 - 2.6 | % | ASTM D955 |
| 23°C | 0.45 - 2.4 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.050 - 0.50 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (23°C) | 29 - 92 | ASTM D2240, ISO 868 | |
| IRHD Hardness | 59 - 85 | ISO 48 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 0.667 - 176 | MPa | ASTM D638 |
| 23°C | 5.20 - 319 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 2.07 - 19.1 | MPa | ASTM D638 |
| Yield, 23°C | 4.50 - 21.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 1.71 - 48.3 | MPa | ASTM D638 |
| Fracture, 23°C | 2.50 - 13.9 | MPa | ISO 527-2 |
| 23°C | 0.0414 - 14.5 | MPa | ASTM D638 |
| 23°C | 2.10 - 16.4 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Fracture, 23°C | 10 - 830 | % | ASTM D638 |
| Fracture, 23°C | 390 - 900 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 200 - 1000 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 5.36 - 390 | MPa | ASTM D790 |
| 23°C | 50.0 - 630 | MPa | ISO 178 |
| Flexural Stress (23°C) | 3.00 - 37.0 | MPa | ISO 178 |
| Taber Abrasion Resistance (23°C) | 1.18 - 374 | mg | ASTM D1044 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Set (23°C) | 3 - 19 | % | ASTM D412 |
| Tensile Stress | |||
| 20% strain, 23°C | 0.500 - 3.10 | MPa | ISO 37 |
| 50% strain, 23°C | 1.17 - 3.18 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.0193 - 5.05 | MPa | ASTM D412 |
| 100% strain, 23°C | 0.940 - 4.15 | MPa | ISO 37 |
| 200% strain, 23°C | 0.276 - 5.34 | MPa | ASTM D412 |
| 300% strain, 23°C | 0.0429 - 7.11 | MPa | ASTM D412 |
| 300% strain, 23°C | 1.47 - 9.46 | MPa | ISO 37 |
| Tensile Strength | |||
| Yield, 23°C | 1.33 - 11.5 | MPa | ASTM D412 |
| Yield, 23°C | 1.73 - 11.5 | MPa | ISO 37 |
| Fracture, 23°C | 2.32 - 14.0 | MPa | ASTM D412 |
| Fracture, 23°C | 2.40 - 18.5 | MPa | ISO 37 |
| 23°C | 2.79 - 7.90 | MPa | ASTM D412 |
| Tensile Elongation | |||
| Yield | 16 - 1100 | % | ASTM D412 |
| Fracture, 23°C | 350 - 900 | % | ASTM D412 |
| Fracture, 23°C | 280 - 850 | % | ISO 37 |
| Tear Strength | |||
| 23°C | 5.25 - 50.1 | kN/m | ASTM D624 |
| 23°C | 2.5 - 42 | kN/m | ISO 34-1 |
| Compression Set | |||
| -- | 11 - 75 | % | ASTM D395 |
| 23°C | 8.7 - 47 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Volume (23°C) | -9.0 - 87 | % | ASTM D471, ISO 1817 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 40.6 - 135 | °C | ASTM D648 |
| Continuous Use Temperature | 105 - 135 | °C | ASTM D794 |
| Brittleness Temperature | |||
| -- | -60.6 - -59.0 | °C | ASTM D746 |
| -- | -67.8 - -50.0 | °C | ISO 812 |
| Vicat Softening Temperature | 40.0 - 207 | °C | ASTM D1525 |
| RTI Elec | 50.0 - 90.0 | °C | UL 746 |
| RTI | 50.0 - 90.0 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | |||
| -- | 3.0 - 8.8E+14 | ohms | ASTM D257 |
| -- | 1.0E+2 - 1.3E+12 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 80 - 1.9E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C) | 24 - 51 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C) | 2.06 - 2.41 | ASTM D150 | |
| Dissipation Factor (23°C) | 1.0E-4 - 0.020 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | 25 - 51 | mm/min | ISO 3795 |
| Glow Wire Flammability Index | 650 - 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | 650 - 850 | °C | IEC 60695-2-13 |
| Oxygen Index | |||
| -- | 18 - 30 | % | ASTM D2863 |
| -- | 25 - 40 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.8 - 94.0 | % | ASTM D1003 |
| Clarity | 93.0 - 95.1 | ASTM D1746 | |
| Haze | 1.0 - 14 | % | ASTM D1003 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity | 0.116 - 193 | Pa·s | ASTM D3835 |
| Melt Viscosity | 100 - 363 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 59.4 - 80.6 | °C | |
| Drying Time | 3.0 - 3.1 | hr | |
| Dew Point | -40.0 - -17.8 | °C | |
| Suggested Max Moisture | 0.019 - 0.10 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 156 - 210 | °C | |
| Middle Temperature | 179 - 216 | °C | |
| Front Temperature | 193 - 223 | °C | |
| Nozzle Temperature | 179 - 226 | °C | |
| Processing (Melt) Temp | 199 - 227 | °C | |
| Mold Temperature | 19.7 - 50.6 | °C | |
| Injection Pressure | 2.24 - 25.9 | MPa | |
| Holding Pressure | 2.10 - 56.1 | MPa | |
| Back Pressure | 0.234 - 3.50 | MPa | |
| Screw Speed | 72 - 75 | rpm | |
| Clamp Tonnage | 3.8 - 3.9 | kN/cm² | |
| Cushion | 14.3 - 14.6 | mm |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPEThis information is provided for comparative purposes only. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 68.3 - 80.3 | °C | |
| Drying Time | 2.4 - 3.1 | hr | |
| Hopper Temperature | 79.0 - 170 | °C | |
| Cylinder Zone 1 Temp. | 142 - 208 | °C | |
| Cylinder Zone 2 Temp. | 179 - 216 | °C | |
| Cylinder Zone 3 Temp. | 170 - 219 | °C | |
| Cylinder Zone 4 Temp. | 160 - 215 | °C | |
| Cylinder Zone 5 Temp. | 180 - 226 | °C | |
| Adapter Temperature | 200 - 205 | °C | |
| Melt Temperature | 193 - 208 | °C | |
| Die Temperature | 183 - 226 | °C |
| Extrusion instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic TPEThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4564 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| SPESIN® KP212G30V0GRS | Kolon Plastics, Inc. | PBT | SPESIN® |
| Axiall PVC 22872 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Edgetek™ AT-000/000 GREY VN-3581 | PolyOne Corporation | Acetal (POM) Copolymer | Edgetek™ |
| LNP™ LUBRILOY™ RX05498 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |