CALIBRE™ 200-14
| Category: | PC , Polycarbonate Resin |
| Manufacturer: | Trinseo |
| Trademark: | CALIBRE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i2qfMs_CALIBRE-200-14.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CALIBRE™ 200-14 polycarbonate resin is a natural, FDA compliant, 14 melt flow rate general purpose polycarbonate resin with no mold release or UV stabilizer. Govt. and Industry Standards:
Applications
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 14 | g/10 min | ASTM D1238, ISO 1133 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 12.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955, ISO 294-4 |
| Water Absorption | ASTM D570, ISO 62 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| M-Scale | 72 | ||
| R-Scale | 118 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2340 | MPa | ASTM D638 |
| -- | 2300 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 60.0 | MPa | ISO 527-2/50 |
| Break 3 | 71.0 | MPa | ASTM D638 |
| Break | 71.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Break 5 | 150 | % | ASTM D638 |
| Break | 150 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break | > 50 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 6 | 2410 | MPa | ASTM D790 |
| -- 7 | 2400 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 8 | 96.5 | MPa | ASTM D790 |
| -- 9 | 97.0 | MPa | ISO 178 |
| Taber Abrasion Resistance | 45 | % | ASTM D1044 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Average Extent of Burning | 3 | cm | ASTM D635 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | |
| 23°C | 80 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact | |||
| 23°C | 850 | J/m | ASTM D256 |
| 23°C | 82 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact (23°C) | No Break | ASTM D256, ISO 180 | |
| Instrumented Dart Impact 10(23°C, Total Energy) | 87.0 | J | ASTM D3763 |
| Tensile Impact Strength | 462 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 143 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 127 | °C | ASTM D648, ISO 75-2/A |
| 1.8 MPa, Annealed | 140 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | 148 | °C | ISO 306/B50, ASTM D1525 11 |
| Ball Indentation Temperature | 125 | °C | IEC 60335-1 |
| CLTE - Flow (-40 to 82°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+18 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149, IEC 60243-1 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 | ||
| Comparative Tracking Index (2.00 mm, Solution A) | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 12 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Glow Wire Ignition Temperature 13(2.00 mm, 5.0 sec) | 849 | °C | IEC 60695-2-13 |
| Oxygen Index 14 | 26 | % | ISO 4589-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542, ISO 489 | |
| Transmittance | 89.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 51 mm/min |
| 5 . | 50 mm/min |
| 6 . | Method I (3 point load), 2.0 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | Method I (3 point load), 2.0 mm/min |
| 9 . | 2.0 mm/min |
| 10 . | 3.39 m/sec |
| 11 . | Rate A (50°C/h), Loading 2 (50 N) |
| 12 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 13 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 14 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rainmaker Polypropylene MCCPCC20 | Rainmaker Polymers LLC | PP Copolymer | Rainmaker Polypropylene |
| VITAMIDE® BH36NT6557 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| apilon 52® 8011 | API SpA | TPU-Polyester | apilon 52® |
| Chemlon® 100 L | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| Fluoroloy® A22 | Saint Gobain Performance Plastics | TP, Unspecified | Fluoroloy® |