Retpol® 7572
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | PolyPacific Pty. Ltd. |
| Trademark: | Retpol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i2GPmp_Retpol-7572.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EPALEX 7572 is a thermoplastic 25% mineral filled polypropylene compound. It is a low flow extrusion grade developed for extremely high impact strength and dimensional stability whilst maintaining a high level of rigidity. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.00 mm) | 0.60 to 1.0 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.00 mm) | 44 | ASTM D785 | |
| Durometer Hardness | ASTM D2240 | ||
| Shore D, 3.00 mm | 70 | ||
| Shore D, 15 sec, 3.00 mm | 61 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(3.00 mm) | 21.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.00 mm) | 470 | % | ASTM D638 |
| Flexural Modulus (3.00 mm) | 2000 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 0°C, 3.00 mm | 570 | J/m | |
| 23°C, 3.00 mm | 860 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 3.00 mm) | 110 | °C | ASTM D648 |
| CLTE - Flow (-30 to 30°C, 3.00 mm) | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 10 | % |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 to 240 | °C | |
| Cylinder Zone 2 Temp. | 180 to 240 | °C | |
| Cylinder Zone 3 Temp. | 180 to 240 | °C | |
| Cylinder Zone 4 Temp. | 180 to 240 | °C | |
| Cylinder Zone 5 Temp. | 180 to 240 | °C | |
| Melt Temperature | 200 to 220 | °C | |
| Die Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2880 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Miramid® S3C | BASF Leuna GmbH | Nylon 66 | Miramid® |
| Mylar® MO 21 (1400 guage) | DuPont Teijin Films U.S. | PET | Mylar® |
| Cheng Yu FV3015 | Cheng Yu Plastic Company Limited | Acetal (POM) Homopolymer | Cheng Yu |
| LNP™ THERMOCOMP™ PF006S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |