SCHULABLEND® (ASA/PA) M/MW NC 100
| Category: | ASA+Nylon , Acrylonitrile Styrene Acrylate + Nylon |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULABLEND® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i23Blx_SCHULABLEND-ASA-PA-M-MW-NC-100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Nanocomposite based on ASA/PA-blend for high dimensional stability |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.18 | -- | g/cm³ | ISO 1183/A |
| Melt Volume-Flow Rate (MVR) (250°C/5.0 kg) | 6.00 | -- | cm³/10min | ISO 1133 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 358/10) | 101 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 3100 | 1900 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Yield) | 51.0 | 34.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 3.1 | 4.7 | % | ISO 527-2/1A/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | ISO 179/1eA |
| 23°C | 10 | 19 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 75 | -- | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 96.0 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 78.0 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | ||||
| -- | 184 | -- | °C | ISO 306/A50 |
| -- | 110 | -- | °C | ISO 306/B50 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (2.00 mm) | 30 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | IEC 60695-11-10, -20 | |
| 3.00 mm | HB | -- | IEC 60695-11-10, -20 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | |||
| 1.50 mm | 675 | -- | °C | IEC 60695-2-12 |
| 3.00 mm | 675 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 1.50 mm | 700 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 700 | -- | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RABALON® SJ4300C | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| Tecomid® NB40 GR30 NL IM | Eurotec Engineering Plastics | Nylon 6 | Tecomid® |
| Ultradur® B 4300 G6 HR Unc. | BASF Corporation | PBT | Ultradur® |
| Niretan A F35 | Soredi S.p.a. | Nylon 66 | Niretan A |
| Polifil® Nylon 620-33GF | The Plastics Group | Nylon 66 | Polifil® Nylon |