RIALFILL B 15 SA 28 TC
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i1EOy3_RIALFILL-B-15-SA-28-TC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound 28% filled with lamellar talc and calcium carbonate; additive in order to forestall the superficial acculation of electrostatic charge. Correct balance between stiffness and toughness; specific product for injection molding of high aethetic particulars for domestic furniture; available in the versions natural and colored as per sample. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 1.1 | % | |
| Ash Content | 28 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 72 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 25.0 | MPa | |
| Break, 23°C | 20.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 8.0 | % | |
| Break, 23°C | 50 | % | |
| Flexural Modulus 1(23°C) | 2200 | MPa | ISO 178 |
| Flexural Stress (23°C) | 36.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 2.5 | kJ/m² | |
| 23°C | 4.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 83.0 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 190 to 210 | °C | |
| Mold Temperature | 40.0 to 50.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POPELEN HSP-375 | Lotte Chemical Corporation | PP Impact Copolymer | POPELEN |
| Sumitomo PP Y101 | Sumitomo Chemical Asia | PP Homopolymer | Sumitomo PP |
| Vyncolit® RX®1366FR-P | Vyncolit N.V. | DAP | Vyncolit® |
| NOVADURAN® 5010G30 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| KYOCERA KE-1100A-S3 | KYOCERA Chemical Corporation | Epoxy | KYOCERA |