Sarlink® TPV 4775B40
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | i11toA_Sarlink-TPV-4775B40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® X4775BLK40 is a black, low hardness UV stable grade possessing superior compression set, chemical resistance and high temperature performance. This product is a high flow material designed for injection molding applications that require superior flow properties. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.908 | g/cm³ | ASTM D792 |
| -- | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shore A, 5 sec, Extruded | 74 | ||
| Shore A, 5 sec, Injection Molded | 76 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Across Flow : 100% Strain | 3.10 | MPa | |
| Flow : 100% Strain | 3.50 | MPa | |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Across Flow : Break | 6.60 | MPa | |
| Flow : Break | 6.00 | MPa | |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Across Flow : Break | 490 | % | |
| Flow : Break | 410 | % | |
| Tear Strength - Across Flow | |||
| -- | 33.3 | kN/m | ASTM D624 |
| -- 1 | 33 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 24 | % | |
| 70°C, 22 hr | 36 | % | |
| 125°C, 70 hr | 52 | % |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air - Across Flow | |||
| 135°C, 1000 hr | -12 | % | ASTM D573, ISO 188 |
| 100% Strain, 135°C, 1000 hr | 5.0 | % | ASTM D573 |
| 150°C, 168 hr | -22 | % | ASTM D573, ISO 188 |
| 100% Strain, 150°C, 168 hr | 2.0 | % | ASTM D573 |
| 100% Strain 135°C, 1000 hr | 5.0 | % | ISO 188 |
| 100% Strain 150°C, 168 hr | 2.0 | % | ISO 188 |
| Change in Ultimate Elongation in Air - Across Flow | ASTM D573, ISO 188 | ||
| 135°C, 1000 hr | -16 | % | |
| 150°C, 168 hr | -29 | % | |
| Change in Durometer Hardness in Air | ASTM D573, ISO 188 | ||
| Shore A, 135°C, 1000 hr | 3.0 | ||
| Shore A, 150°C, 168 hr | 1.0 | ||
| Change in Volume (125°C, 70 hr, in IRM 903 Oil) | 74 | % | ASTM D471, ISO 1817 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary @ 206/s | |||
| 200°C | 220 | Pa·s | ISO 11443 |
| 200°C | 220 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 to 216 | °C | |
| Middle Temperature | 177 to 216 | °C | |
| Front Temperature | 177 to 216 | °C | |
| Nozzle Temperature | 188 to 221 | °C | |
| Processing (Melt) Temp | 182 to 221 | °C | |
| Mold Temperature | 10.0 to 65.6 | °C | |
| Back Pressure | 0.0689 to 1.03 | MPa | |
| Screw Speed | 100 to 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Method Ba, Angle (Unnicked) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Reny® 2620 | Mitsubishi Engineering-Plastics Corp | PARA | Reny® |
| SCHULADUR® A1 GF 30 LW | A. Schulman Europe | PBT+PET | SCHULADUR® |
| ULTEM™ D9065 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| CERTENE™ LDF-0422J | Muehlstein | LDPE | CERTENE™ |
| Huafon JF-HSY-9580 | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |