TECHNYL STAR® S 60G1 V30 BLACK 15 N Datasheet,Nylon 6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL STAR® S 60G1 V30 Black 15N is a Non-halogenated flame retardant grade based on a patented high flow polyamide 6 resin (TechnylStar), reinforced of 30% of glass fiber, heat stabilized, for injection moulding. This grade is Heat stabilized and provides optimized injection moulding performance.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 30% filler by weight
Additive	heat stabilizer Flame retardancy
Features	Excellent appearance Anti-arc Good corrosion resistance High liquidity Low temperature impact resistance Good demoulding performance Halogen-free
Uses	Electrical/Electronic Applications Connector
Agency Ratings	EC 1907/2006 (REACH) EN 45545 NF F 16-101 UL QMFZ2
RoHS Compliance	RoHS compliance
Appearance	Black Grey Natural color
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA6-GF30 FR(40)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.42	--	g/cm³	ISO 1183/A
Water Absorption				ISO 62
23°C, 24 hr	0.87	--	%	ISO 62
Saturated, 23°C	4.0	--	%	ISO 62
Equilibrium, 23°C, 50% RH	1.7	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	10600	7700	MPa	ISO 527-2/1A
Tensile Strength
Fracture, 23°C	133	--	MPa	ASTM D638
Fracture, 23°C	147	97.0	MPa	ISO 527-2/1A
Tensile Elongation
Fracture, 23°C	2.6	--	%	ASTM D638
Fracture, 23°C	2.1	4.0	%	ISO 527-2
Flexural Modulus
23°C	9870	--	MPa	ASTM D790
23°C	9600	5600	MPa	ISO 178
Flexural Strength
23°C	200	--	MPa	ASTM D790
23°C	230	151	MPa	ISO 178

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength				ISO 179/1eA
-30°C	8.5	--	kJ/m²	ISO 179/1eA
23°C	9.0	12	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength				ISO 179/1eU
-30°C	43	--	kJ/m²	ISO 179/1eU
23°C	56	59	kJ/m²	ISO 179/1eU
Notched Izod Impact
23°C	90	--	J/m	ASTM D256
23°C	9.0	11	kJ/m²	ISO 180
Unnotched Izod Impact Strength (23°C)	50	55	kJ/m²	ISO 180/1U

Thermal	Dry	Conditioned	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, not annealed	205	--	°C	ASTM D648
1.8 MPa, not annealed	205	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Surface Resistivity	6.0E+14	--	ohms	IEC 60093
Volume Resistivity	1.0E+15	--	ohms·cm	IEC 60093
Dielectric Strength				IEC 60243-1
0.800 mm	38	--	kV/mm	IEC 60243-1
2.00 mm	25	23	kV/mm	IEC 60243-1
Relative Permittivity	2.90	4.35		IEC 60250
Dissipation Factor	--	0.080		IEC 60250
Comparative Tracking Index (Solution A)	600	600	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.40 mm	V-0	--		UL 94
0.8 mm	V-0	--		UL 94
1.6 mm	V-0 5VA	--		UL 94
3.2 mm	V-0 5VA	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
0.8 mm	960	--	°C	IEC 60695-2-12
1.6 mm	960	--	°C	IEC 60695-2-12
3.2 mm	960	--	°C	IEC 60695-2-12
Glow Wire Ignition Temperature				IEC 60695-2-13
0.8 mm	775	--	°C	IEC 60695-2-13
1.6 mm	800	--	°C	IEC 60695-2-13
3.2 mm	825	--	°C	IEC 60695-2-13
Oxygen Index	35	--	%	ISO 4589-2
French Fire Index	F2	--		NF F16-101
French Smoke Index	I3	--		NF F16-101

Additional Information	Dry	Conditioned	Test Method
European Railways Certifications			EN 45545-2
R22	HL2	--	EN 45545-2
R23	HL3	--	EN 45545-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	240 - 245	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time. The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL STAR®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	i0qLss_TECHNYLSTARS60G1V30BLACK15N.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
RTP 1000 HI FR A	RTP Company	PBT	RTP
VAMPLUB C 20G 2TF	Vamp Tech	PC	VAMPLUB
Braskem PE ES6007	Braskem	HDPE	Braskem PE
Perfactory® Clear Guide	EnvisionTEC, Inc.	Unspecified	Perfactory®
Petlon Prime A2-G30-00-NT	Petlon Polymers Ltd	Nylon 6	Petlon Prime