Polytron® A30N02
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | Polytron® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hzpumF_Polytron-A30N02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% LONG FIBER GLASS REINFORCED NATURAL NYLON 6.6 HEAT STABILIZED,UV STABILIZED FOR INJECTION MOULDING APPLICATION. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.30 | % | ASTM D955 |
| -- | 0.20 to 0.30 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 3.4 | % | ASTM D570 |
| Saturation, 23°C | 3.4 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.0 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 10700 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 150 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 10000 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 250 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 60 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 220 | J/m | ASTM D256 |
| 23°C | 22 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 255 | °C | ASTM D648, ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® LL6F 809-HSB | Marco Polo International, Inc. | LLDPE | MARPOL® |
| Quadraflex™ ALE-55D | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| Sasol Polymers PE LT033 (Extrusion/Blow molding) | Sasol Polymers | LDPE | Sasol Polymers PE |
| Ultralloy™ 911 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| MAJORIS G209 BLACK 8229 | AD majoris | PP, Unspecified | MAJORIS |