LNP™ LUBRICOMP™ Noryl_SPN422L compound
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hyN55i_LNPLUBRICOMPNorylSPN422Lcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP NORYL_SPN422L is a wear resistant, fluorocarbon alloy, 235F (113C) HDT. UL94 HB rated. Check surface aesthetics prior to material specification. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow 1 | 0.50 - 0.70 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(Yield) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break) | 35 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2280 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 75.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 96 | J/m | ASTM D256 |
| 23°C | 270 | J/m | ASTM D256 |
| Dart Drop Impact (23°C) | 13.6 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 113 | °C | ASTM D648 |
| RTI Elec | 50.0 | °C | UL 746 |
| RTI Imp | 50.0 | °C | UL 746 |
| RTI | 50.0 | °C | UL 746 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 2 | UL 746 | |
| High Amp Arc Ignition (HAI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 3 | UL 746 | |
| Hot-wire Ignition (HWI) | PLC 2 | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.47 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 249 - 299 | °C | |
| Middle Temperature | 260 - 304 | °C | |
| Front Temperature | 271 - 310 | °C | |
| Nozzle Temperature | 282 - 310 | °C | |
| Processing (Melt) Temp | 282 - 310 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene TPP1040 | Teknor Apex Asia Pacific PTE. LTD. | PP Homopolymer | Sinpolene |
| VESTAMID® HTplus M1036 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| Geon™ Vinyl Flexible A48248D | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| INELEC PEASFC | Infinity LTL Engineered Compounds | PE, Unspecified | INELEC |
| OmniLon™ PA6/6 U IM20 HS BK1000 | OMNI Plastics, LLC | Nylon 66 | OmniLon™ |