Hifax TRC 770P
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hyMoXs_Hifax-TRC-770P.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax TRC 770P high melt flow, 1,600 MPa flexural modulus, UV-stabilized, mineral-filled, precolored thermoplastic elastomeric olefin (TEO) resin has an excellent balance of properties and processability. It was designed primarily for use in molded-in color automotive bumper fascias. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 28 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 19.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 7.0 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 1600 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 5.8 | kJ/m² | |
| 23°C | 32 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Unilex™ UP.4400.952 | United Polychem | HDPE | Unilex™ |
| Golden Compound PP S²PC 3545 BO 15IM16 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Iupilon® EGN2020DR 9913A | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| LubriOne™ ATH-000/04S NATURAL | PolyOne Corporation | Acetal (POM) Homopolymer | LubriOne™ |
| DEXFLEX® 815 BLK XXX | LyondellBasell Industries | TPO (POE) | DEXFLEX® |