Desmovit® DP R 9929
| Category: | TPU-Ester/Ether , Thermoplastic Polyurethane Elastomer (Ester/Ether) |
| Manufacturer: | geba Kunststoffcompounds GmbH |
| Trademark: | Desmovit® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hxsgAR_Desmovit-DP-R-9929.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| High stiffness, very good impact resistance and flexibility even at low temperatures - these are the strengths of new glass fibre reinforced polyetherdiol based thermoplastic polyurethanes (TPUs |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.32 | g/cm³ | ISO 1183/A |
| Molding Shrinkage | |||
| Across Flow | 0.38 | % | |
| Flow | 0.13 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 71.0 | MPa | ISO 527-2/200 |
| Tensile Strain (Break) | 8.0 | % | ISO 527-2/200 |
| Flexural Modulus 1 | ISO 178 | ||
| -30°C | 4300 | MPa | |
| 23°C | 2900 | MPa | |
| Flexural Stress 2 | ISO 178 | ||
| -30°C | 154 | MPa | |
| 23°C | 78.0 | MPa | |
| Abrasion | 83 | mm³ | ISO 4649 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | |
| 23°C | 26 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 82 | kJ/m² | |
| 23°C | 75 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 161 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 104 | °C | ISO 306/B50 |
| CLTE | DIN 53752 | ||
| Flow | 9.6E-6 | cm/cm/°C | |
| Transverse | 1.2E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 120 to 130 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 200 to 230 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| BP PPC 0212 BLK | Buckeye Polymers, Inc. | PP Copolymer | BP |
| Ferro PP CPP30GF15NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Fusabond® P353 | DuPont Packaging & Industrial Polymers | PP, Unspecified | Fusabond® |
| Iupiace® TX403 | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |
| Karina IVORY PVC COMPOUND -E 854-35/ 1-D-IS(VS-90)/K | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |