Andur 9500 APLF/Curene® 442
| Category: | PUR-Ether/TDI , Polyurethane (Polyether, TDI) |
| Manufacturer: | Anderson Development Company |
| Trademark: | Andur |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hvmLed_Andur-9500-APLF-Curene-442.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Andur 9500 APLF is a polyether (PPG) based liquid, toluene diisocyanate terminated prepolymer containing 0.1% or less free TDI monomer. An elastomer with a hardness of 95 Shore A is obtained when this prepolymer is cured with Curene 442 [4,4'-methylene-bis (orthochloroaniline)]. Elastomers of lower hardness can be obtained by curing Andur 9500 APLF with polyols and their combination with Curene 442 and other diamines, or by the use of plasticizers. |
| General Information | |
|---|---|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.13 | g/cm³ | ASTM D1505 |
| Molding Shrinkage - Flow | 1.5 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 95 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Compressive Strength | ASTM D695 | ||
| 5% strain | 1.36 | MPa | ASTM D695 |
| 10% strain | 4.55 | MPa | ASTM D695 |
| 15% strain | 7.25 | MPa | ASTM D695 |
| 25% strain | 10.4 | MPa | ASTM D695 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 13.8 | MPa | ASTM D412 |
| 300% strain | 20.3 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 29.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 400 | % | ASTM D412 |
| Compression Set | 35 | % | ASTM D395B |
| Bayshore Resilience | 35 | % | ASTM D2632 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Pot Life | 5.0 - 6.0 | min | |
| Demold Time | 20 - 30 | min | |
| Post Cure Time (96°C) | 16 | hr |
| Additional Information |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 93 to 97Die C Tear, ASTM D1004: 350 pliAverage Split Tear, ASTM D1938: 130 pliStoichiometry Curative Level: 95%Grams Curene 442 per 100 grams Andur 9500 APLF: 17.5 to 18.7Mix Temperature: Andur 9500 APLF: 150-180°F Curene 442: 230-240°F |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 100 - 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mecoline IS RDX 5243 F | Melos GmbH | TP, Unspecified | Mecoline |
| SPESIN® KP212G30VFBL | Kolon Plastics, Inc. | PBT | SPESIN® |
| ELASTOSIL® LR 3005/30 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| Keltan® 8570 | LANXESS Buna GmbH | EPDM | Keltan® |
| Sylvin 9067-80 RED 604 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |