Styrolution PS 476L
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | INEOS Styrolution Group GmbH |
| Trademark: | Styrolution PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hvZFKg_Styrolution-PS-476L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Styrolution PS 476L is a normal flow and very high impact Polystyrene. It gives good mechanical and heat resistance properties while providing with easy processability and short cycle time. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (200°C/5.0 kg) | 5.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | 0.40 to 0.70 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | < 0.10 | % | |
| Equilibrium, 23°C, 50% RH | < 0.10 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 85.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1850 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 27.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield, 23°C | 1.5 | % | |
| Break, 23°C | 30 | % | |
| Flexural Modulus | 1950 | MPa | ISO 178 |
| Flexural Stress | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 130 | kJ/m² | |
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 11 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Annealed | 89.0 | °C | ISO 75-2/B |
| 1.8 MPa, Annealed | 80.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 98.0 | °C | ISO 306/A50 |
| -- | 90.0 | °C | ISO 306/B50 |
| CLTE - Flow | 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+18 | ohms·cm | IEC 60093 |
| Electric Strength 1(1.50 mm) | 160 | kV/mm | IEC 60243-1 |
| Dielectric Constant | |||
| 100 Hz | 2.50 | IEC 60250 | |
| 1 MHz | 2.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 4.0E-4 | IEC 60250 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60°) | 35 | ASTM D523 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 260 | °C | |
| Mold Temperature | 10.0 to 60.0 | °C | |
| Injection Velocity | 200 | mm/sec |
| Note Message | |
|---|---|
| 1 . | Short Time |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AIE PC/ABS A2200FR-2950 | Asia International Enterprise (Hong Kong) Limited | PC+ABS | AIE PC/ABS |
| Beamset 770 | Arakawa Chemical Industries, Ltd. | Vinyl Ester | Beamset |
| Gallonprene® GP520-4005 | Shenzhen Sungallon Rubber & Plastic Corporation Limited | TPE | Gallonprene® |
| Hifax TRC 779X SHS BLACK | LyondellBasell Industries | PP, Unspecified | Hifax |
| LNP™ LUBRICOMP™ AL003 compound | SABIC Innovative Plastics | ABS | LNP™ LUBRICOMP™ |