Alkamax® ML2610PN
| Category: | mLLDPE , Metallocene Linear Low Density Polyethylene |
| Manufacturer: | Qenos Pty Ltd |
| Trademark: | Alkamax® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hvRD81_Alkamax-ML2610PN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Alkamax® ML2610PN is a metallocene linear low density polyethylene copolymer. This metallocene grade has excellent processability permitting higher production rates and is designed for high performance film applications requiring superior toughness and stiffness. Alkamax® ML2610PN is formulated with a process aid and a process stabilisation package. It does not contain slip or antiblocking additives. Alkamax® ML2610PN is intended for applications requiring high performance polyethylene resins. Films produced with Alkamax® ML2610PN have superior stiffness and toughness, which may allow downgauging existing film structures. These properties combined with excellent optical properties and high performance sealing make this grade ideal for heavy duty applications, lamination and form, fill and seal films. It has been designed for processing on a wide range of blown film extrusion equipment. Addition of a UV stabiliser should be considered where the intended application involves intermittent to extended exposure to sunlight. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.926 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 2% Secant, MD : 50 µm | 250 | MPa | |
| 2% Secant, TD : 50 µm | 270 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield, 50 µm | 14.0 | MPa | |
| TD : Yield, 50 µm | 14.0 | MPa | |
| MD : Break, 50 µm | 46.0 | MPa | |
| TD : Break, 50 µm | 45.0 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break, 50 µm | 840 | % | |
| TD : Break, 50 µm | 900 | % | |
| Dart Drop Impact 4 | > 350 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm | 470 | g | |
| TD : 50 µm | 600 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss 5(45°) | 53 | ASTM D2457 | |
| Haze 6(50.0 µm) | 15 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 20 mm/min |
| 2 . | 500 mm/min |
| 3 . | 500 mm/min |
| 4 . | F50 |
| 5 . | (10% LDPE blended) |
| 6 . | (10% LDPE blended) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 548B V15 BLACK 23 N | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® A |
| Ultron® 150 | Asia International Enterprise (Hong Kong) Limited | PEI | Ultron® |
| EMLON® 6 HV | EMAS Plastik San.Tic.AS. | Nylon 6 | EMLON® |
| Paxon™ 7000 XL Series | ExxonMobil Chemical | HDPE, UHMW | Paxon™ |
| Sylvin 2900-70 Clear 8382 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |