ALCUDIA® EBA CA-3430B
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® EBA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hvHprl_ALCUDIA-EBA-CA-3430B.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EBA ALCUDIA® CA-3430B is stabilized with HALS (colourless), UV absorber and antioxidants. This compound offers high solar radiation resistance. APLICATIONS Films for greenhouses and tunnels cover. The 200 µm thickness films made with ALCUDIA® CA-3430B have a lifetime of three continuous agricultural seasons (three winters and two summers) in geographical areas where the maximum solar radiation is 160 Kly. For further information, contact to Technical Assistance and Development Department or Commercial Attention Service. Recommended melt temperature range from 190 to 210°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.928 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| n-Butyl Acrylate Content | 8.0 | wt% |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 200 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 21.0 | MPa | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 21.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Fracture, 200 µm, blown film | 590 | % | ISO 527-3 |
| TD : Fracture, 200 µm, blown film | 600 | % | ISO 527-3 |
| Dart Drop Impact (200 µm, blown film) | 1700 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 200 µm, blown film | 10 | N | ISO 6383-2 |
| TD : 200 µm, blown film | 12 | N | ISO 6383-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (200 µm, blown film) | 20 | % | ASTM D1003 |
| Global Transmission of Visible Light 1(200.0 µm) | 91 | % | EN 13206 |
| Additional Information |
|---|
| Data taken from 200 µm thickness film. Blown up ratio of 2.25:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 190 - 210 | °C |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris ABS LHF491 | Sincerity Australia Pty Ltd. | ABS | Sindustris ABS |
| Adell Polyamide BJ-33 Impact Modified | Adell Plastics, Inc. | Nylon 6 | Adell Polyamide |
| ACRYREX® CM-205 | CHI MEI CORPORATION | Acrylic (PMMA) | ACRYREX® |
| apilon 52® 5011 | API SpA | TPU-Polyester | apilon 52® |
| Fixmaster Urethane Liquid | Loctite® | PUR, Unspecified | Fixmaster |