SCHULARENE™ N3103
| Category: | PLA , Polylactic Acid |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULARENE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | huCcGh_SCHULARENEN3103.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Schularene™ N3103 is a high heat PLA. This material achieves a higher heat deflection temperature as standard PLA. The heat performance is similar to PS, PP and ABS. As powder it's used for laminating adhesive in textile or automotive applications. We recommend for most applications pre-drying before processing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.24 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 30 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ASTM D638 |
| Tensile Strength | 45.0 | MPa | ASTM D638 |
| Tensile Strain (Break) | 5.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 105 | °C | ISO 75-2/B |
| Peak Melting Temperature | 190 - 220 | °C | DSC |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRF3705E | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Hoffman PVC V7-54 | Hoffman Plastic Compounds Inc. | PVC, Rigid | Hoffman PVC |
| ICORENE® 9993 | ICO Polymers EMEA, A Division of A. Schulman | PVDF | ICORENE® |
| Jampilen H1022 | Jam Polypropylene Company | PP Copolymer | Jampilen |
| Karina GRAY PVC COMPOUND 805-18/105-IS-SD | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |