Lustran ABS 752 resin is a high-gloss, high-impact extrusion grade of ABS (Acrylonitrile Butadiene Styrene). In its natural color (000000), Lustran ABS 752 meets FDA requirements for food contact.** It also provides a superior balance between rigidity and impact strength, as well as excellent melt strength for good thermoformability. It is easy to color with ABS color concentrates. Lustran ABS 752 resin is used for extrusion applications that require high-impact toughness. Typical applications include various carrying cases, table tops, wall panels, and profiles. It is also used as a substrate under other specialty grades, such as Lustran ABS 556 low-gloss resin. As with any product, use of Lustran ABS 752 resin in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Specific Volume | 0.960 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 230°C/10.0 kg | 7.7 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 1.7 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 102 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| -18°C | 2070 | MPa | ASTM D638 |
| 23°C | 1860 | MPa | ASTM D638 |
| 71°C | 1310 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, -18°C | 51.0 | MPa | ASTM D638 |
| Yield, 23°C | 35.2 | MPa | ASTM D638 |
| Yield, 71°C | 19.3 | MPa | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| -40°C | 2410 | MPa | ASTM D790 |
| 23°C | 1860 | MPa | ASTM D790 |
| 71°C | 1520 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Yield, -40°C | 89.6 | MPa | ASTM D790 |
| Yield, 23°C | 55.2 | MPa | ASTM D790 |
| Yield, 71°C | 41.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.18 mm | 180 | J/m | ASTM D256 |
| -18°C, 3.18 mm | 240 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 370 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -40°C, Peak Energy | 28.5 | J | ASTM D3763 |
| -40°C, 3.18 mm, Total Energy | 31.2 | J | ASTM D3763 |
| -18°C, Peak Energy | 31.2 | J | ASTM D3763 |
| -18°C, Total Energy | 40.7 | J | ASTM D3763 |
| 23°C, Peak Energy | 27.1 | J | ASTM D3763 |
| 23°C, Total Energy | 46.1 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.18mm | 91.1 | °C | ASTM D648 |
| 0.45 MPa, annealed, 3.18mm | 98.9 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.18mm | 83.9 | °C | ASTM D648 |
| 1.8 MPa, annealed, 3.18mm | 92.2 | °C | ASTM D648 |
| CLTE - Flow | 9.4E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (0.762 mm) | 60.0 | °C | UL 746 |
| RTI Imp (0.762 mm) | 60.0 | °C | UL 746 |
| RTI (0.762 mm) | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(3.18 mm) | 36 | mm/min | ASTM D635 |
| Flame Rating (1.50 mm) | HB | UL 94 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gardner Gloss (60 °, extruded sheet) | 90 | ASTM D523 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 - 93.3 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | < 0.030 | % | |
| Cylinder Zone 1 Temp. | 216 - 241 | °C | |
| Cylinder Zone 2 Temp. | 218 - 241 | °C | |
| Cylinder Zone 3 Temp. | 218 - 241 | °C | |
| Cylinder Zone 4 Temp. | 218 - 241 | °C | |
| Cylinder Zone 5 Temp. | 218 - 241 | °C | |
| Melt Temperature | 216 - 249 | °C | |
| Die Temperature | 210 - 241 | °C | |
| Take-Off Roll | 62.8 - 104 | °C |
| Extrusion instructions |
|---|
| Max. Regrind Allowed: 40% |
| Note Message | |
|---|---|
| 1 . | Injection Molded specimen |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sevrene® 3000-60A | Vi-Chem Corporation | TPE | Sevrene® |
| Sylvin 8757-60LG Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Arak LLDPE HD3840UA | Shazand (Arak) Petrochemical Corporation | LMDPE | Arak LLDPE |
| LUVOCOM® 80-7917 VP | Lehmann & Voss & Co. | Acetal (POM) Copolymer | LUVOCOM® |
| LEXAN™ PC1000R resin | SABIC Innovative Plastics | PC | LEXAN™ |