Sarlink® TPE EE-2250N NAT
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | htZPTS_Sarlink-TPE-EE-2250N-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| The Sarlink EE-2200 series UV Resistant extrusion grades suitable for automotive exterior applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.17 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.40 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ISO 868 | ||
| Shaw A | 53 | ISO 868 | |
| Shaw A, 15 seconds | 50 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flexural Modulus | 10.0 | MPa | ASTM D790 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 37 | ||
| Transverse flow : 100% strain | 1.17 | MPa | ISO 37 |
| Flow : 100% strain | 1.76 | MPa | ISO 37 |
| Tensile Stress | ISO 37 | ||
| Transverse flow : Fracture | 6.86 | MPa | ISO 37 |
| Flow : Fracture | 4.52 | MPa | ISO 37 |
| Tensile Elongation | ISO 37 | ||
| Transverse flow : Fracture | 870 | % | ISO 37 |
| Flow : Fracture | 690 | % | ISO 37 |
| Tear Strength - Across Flow | 25 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 22 hr | 15 | % | ISO 815 |
| 70°C, 22 hr | 30 | % | ISO 815 |
| 125°C, 70 hr | 76 | % | ISO 815 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Viscosity (200°C, 206 sec^-1) | 210 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Rear Temperature | 199 - 210 | °C | |
| Middle Temperature | 204 - 216 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Nozzle Temperature | 216 - 227 | °C | |
| Processing (Melt) Temp | 216 - 227 | °C | |
| Mold Temperature | 35.0 - 65.6 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| 无需干燥。但如果湿度过大，则将粒料在150°F (65°C)的温度下干燥2-4小时。 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 193 - 204 | °C | |
| Cylinder Zone 2 Temp. | 199 - 210 | °C | |
| Cylinder Zone 3 Temp. | 204 - 216 | °C | |
| Cylinder Zone 5 Temp. | 210 - 221 | °C | |
| Die Temperature | 216 - 227 | °C |
| Extrusion instructions |
|---|
| 螺杆转速30 - 100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Baytec® MS-051 (HQEE) | Covestro - PUR | PUR-Ester/MDI | Baytec® |
| Foam-It® 8 | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| Hostacom TRC 411N | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Karina CREPE PVC COMPOUND -E 601D22/ 15 | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Optical POQ62 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |