Latigray 53/22-01 CX/25
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latigray |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hrxH62_Latigray-53-22-01-CX-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Radiopaque compound based on Polypropylene homopolymer (PPh), impact modified. Special mineral filler. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.2 to 1.5 | % | |
| Flow : 2.00 mm | 1.1 to 1.4 | % | |
| Water Absorption (23°C, 24 hr) | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 2600 | MPa | |
| 60°C | 1100 | MPa | |
| 90°C | 650 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 23°C | 25.0 | MPa | |
| Yield, 60°C | 20.0 | MPa | |
| Yield, 90°C | 10.0 | MPa | |
| Break, 23°C | 18.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 23°C | 6.0 | % | |
| Yield, 60°C | 8.5 | % | |
| Yield, 90°C | 9.0 | % | |
| Break, 23°C | > 100 | % | |
| Break, 60°C | > 100 | % | |
| Break, 90°C | > 100 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 1.0 | kJ/m² | |
| 23°C | 3.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 15 | kJ/m² | |
| 23°C | 65 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 105 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 55.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 120 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 8.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | HB | ||
| 1.50 mm | HB | ||
| Glow Wire Flammability Index (1.00 mm) | 750 750 | °C | IEC 60695-2-12 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Dimensional Stability | 73.0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 220 to 240 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 60 MPa |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW0442 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| TECHLEN H2402 | DAEHA Co., LTD | PP, Unspecified | TECHLEN |
| Hostacom TRC 454N D11534 | LyondellBasell Industries | PP, Unspecified | Hostacom |
| Lucky Enpla LKFR | Lucky Enpla Co LTD | ABS | Lucky Enpla |
| Sylvin 9266-70 Blue 8417 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |