Quadrant EPP TIVAR® 88 ESD
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hrV39K_Quadrant-EPP-TIVAR-88-ESD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP TIVAR® 88 ESD is an Ultra High Molecular Weight Polyethylene product filled with glass fiber. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.945 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 67 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 772 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 33.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Flexural Modulus | 772 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 22.8 | MPa | ASTM D790 |
| Compressive Modulus | 600 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 20.7 | MPa | ASTM D695 |
| Coefficient of Friction (vs. Steel - Static) | 0.14 | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 1 | 0.0701 | MPa·m/s | Internal Method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Crystallization Temperature (DSC) | 135 | °C | ASTM D3418 |
| CLTE - Flow 2(-40 to 149°C) | 3.2E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+6 to 1.0E+9 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 4:1 safety factor |
| 2 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TUFNYL® SGF 40 NATURAL | SRF Ltd. | Nylon 6 | TUFNYL® |
| Andur 7501 DPLF/Curene® 442 | Anderson Development Company | PUR-Ether/TDI | Andur |
| PERCOM® MCS12U | A. Schulman Europe | PP Copolymer | PERCOM® |
| LUVOCOM® 1106-8892 | LEHVOSS Group | PEI | LUVOCOM® |
| LNP™ LUBRICOMP™ KG002 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ LUBRICOMP™ |