Indothene HD 52GF004
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | Indothene HD |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hrNfxZ_Indothene-HD-52GF004.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Indothene-HD grade 52GF004 is a blown film grade of High Molecular Weight High Density Polyethylene (HM-HDPE), produced by Hostalen Stirred Tank Heavy Diluent(STHD) Slurry process at Gandhar. It possesses broad molecular weight distribution, which improves processability. 52GF004 can readily be processed on HMHDPE blown film extrusion lines. The films will have homogeneous, finely textured, opaque appearance and exhibit balanced mechanical properties and very good gloss. FOOD CONTACT APPLICATIONS : This grade meets the requirements of Indian Standard IS-10146-1982 on "Polyethylene for its safe use in contact with food stuffs, pharmaceuticals and drinking water". It also conforms to the positive list of constituents as approved in IS:10141:1982. The grade complies with FDA regulation: CFR title 21 , 177.1520, Olefin polymer |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/21.6 kg | 8.5 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.45 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 20 µm, blown film | 31.0 | MPa | ASTM D882 |
| TD : Yield, 20 µm, blown film | 29.0 | MPa | ASTM D882 |
| MD : Broken, 20 µm, blown film | 50.0 | MPa | ASTM D882 |
| TD : Broken, 20 µm, blown film | 45.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 20 µm, blown film | 500 | % | ASTM D882 |
| TD : Broken, 20 µm, blown film | 630 | % | ASTM D882 |
| Dart Drop Impact 1(20 µm, Blown Film) | 7.0 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 20 µm, blown film | 0.40 | g | ASTM D1922 |
| TD : 20 µm, blown film | 12 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 200 | °C | |
| Cylinder Zone 3 Temp. | 210 | °C | |
| Cylinder Zone 4 Temp. | 220 | °C | |
| Die Temperature | 215 | °C |
| Extrusion instructions |
|---|
| Blow up ratio: 3 to 5Neck height: 6D to 8D (D-Die dia) |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BZM 23 G9 | Arkema | Nylon 11 | Rilsan® |
| TORZEN® G4300HSL NC01 | INVISTA Engineering Polymers | Nylon 66 | TORZEN® |
| HAIPLEN EP100 CM5 | Taro Plast S.p.A. | PP Copolymer | HAIPLEN |
| GS Pla® AD92W | Mitsubishi Chemical Performance Polymers, Inc. | Biodeg Polymers | GS Pla® |
| Petrotene® PP A3 G30 PRTA011 PH360 MSP | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |