INSTRUC PPGB10HF
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Infinity LTL Engineered Compounds |
| Trademark: | INSTRUC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hqlzob_INSTRUC-PPGB10HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 10% GLASS BEAD FILLED, HIGH FLOW POLYPROPYLENE |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.968 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.18 mm) | 1.4 to 1.9 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 27.6 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 10 | % | ASTM D638 |
| Flexural Modulus | 1380 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact | 690 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 57.2 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+17 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 2.0 | hr | |
| Processing (Melt) Temp | 227 | °C | |
| Mold Temperature | 37.8 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 40 to 70 | rpm | |
| Vent Depth | 0.013 to 0.025 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PTS SAN-82TR | Polymer Technology and Services, LLC | SAN | PTS |
| NOVADURAN® 5010G30X4 | Mitsubishi Engineering-Plastics Corp | PBT | NOVADURAN® |
| BP Flex A 6410 NAT | Buckeye Polymers, Inc. | TPE | BP Flex |
| Braskem PP H 306 | Braskem | PP Homopolymer | Braskem PP |
| LNP™ STAT-KON™ DX09301C compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ STAT-KON™ |