SECCO HIPS-622S
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Shanghai SECCO Petrochemical Co., Ltd |
| Trademark: | SECCO |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hoWCSM_SECCOHIPS622S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HIPS632E retains good impact strength and improved environmental stress crack resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 3.6 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.40 - 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | < 0.10 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 97 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 26.0 | MPa | ISO 527-2/50 |
| Fracture | 25.0 | MPa | ISO 527-2/50 |
| Nominal Tensile Strain at Break | 60 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1650 | MPa | ISO 178 |
| Flexural Stress 2 | 40.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 11 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature 3 | 90.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | in Oil |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Riblene® FC 40 F | Versalis S.p.A. | LDPE | Riblene® |
| RTP ESD A 205 | RTP Company | Nylon 66 | RTP |
| NYCOA Polyamide 2038 | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| KPOL-PP K-PPH 10.0 | KPOL Chem Co. | PP Homopolymer | KPOL-PP |
| PEARLCOAT® 161K | Lubrizol Advanced Materials, Inc. | TPU-Polyether | PEARLCOAT® |