LNP THERMOCOMP MF002AS is a compound based on Polypropylene resin containing Glass Fiber. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound MF-1002 HS Product reorder name: MF002AS |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.970 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 3240 | MPa | ASTM D638 |
| Tensile Strength (Break) | 45.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.7 | % | ASTM D638 |
| Flexural Modulus | 2850 | MPa | ASTM D790 |
| Flexural Strength | 68.9 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 37 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 390 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 129 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsan® BESNO P10 TL | Arkema | Nylon 11 | Rilsan® |
| NYCOA Polyamide ASN 27 330 KNF | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Capilene® HU 75 AV | Carmel Olefins Ltd. | PP Impact Copolymer | Capilene® |
| Diaterm® A27 GF30TF10 | DTR S.r.l. (Develop Thermoplastic Resins) | Nylon 6 | Diaterm® |
| Osterlene® LLSH0917 | Osterman & Company | LLDPE | Osterlene® |