Jamplast Inj-03 ABS
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hnQHu3_Jamplast-Inj-03-ABS.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Jamplast Inj-03 ABS is a general injection molding grade of ABS (Acrylonitrile Butadiene Styrene). It is a high-impact, high-gloss ABS, available only in natural and black. Typical applications include housings, toys, small appliances, and cusumer goods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.05 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 220°C/10.0 kg | 12 | g/10 min | ASTM D1238 |
| 230°C/3.8 kg | 5.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 109 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2550 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | > 30 | % | ASTM D638 |
| Flexural Modulus | 2600 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C, 3.20 mm | 64 | J/m | ASTM D256 |
| 23°C, 3.20 mm | 380 | J/m | ASTM D256 |
| 23°C, 12.7 mm | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 12.7mm | 92.0 | °C | ASTM D648 |
| 0.45 MPa, annealed, 12.7mm | 99.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 85.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm, molded | 102 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 94.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 106 | °C | ASTM D1525 |
| CLTE - Flow | 9.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.0 - 77.0 | °C | |
| Drying Time | 4.0 | hr | |
| Dew Point | 29.0 | °C | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 235 - 249 | °C | |
| Middle Temperature | 241 - 254 | °C | |
| Front Temperature | 246 - 260 | °C | |
| Nozzle Temperature | 246 - 260 | °C | |
| Processing (Melt) Temp | 246 - 274 | °C | |
| Mold Temperature | 43.0 - 66.0 | °C | |
| Injection Pressure | 68.9 - 110 | MPa | |
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 3.1 - 6.2 | kN/cm² | |
| Cushion | < 6.35 | mm |
| Injection instructions |
|---|
| Alternative Drying Recomendations82.0 - 88.0 °C @ 7200 sec. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SV-0167 | SAMSUNG SDI CO., LTD. | ABS | Starex |
| APEX® 2075 | Teknor Apex Company | PVC, Flexible | APEX® |
| INEOS PP R01A-00 | INEOS Olefins & Polymers USA | PP Random Copolymer | INEOS PP |
| LEXAN™ ML3729 resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Karina IVORY PVC COMPOUND 75920-35/1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |