Latamid 66 E21 G/30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latamid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hmrUn8_Latamid-66-E21-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polyamide 66 (PA 66). Toughened. Glass fibres. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.2 | % | |
| Flow : 2.00 mm | 0.45 to 0.75 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8000 | MPa | |
| 60°C | 5700 | MPa | |
| 90°C | 4100 | MPa | |
| 120°C | 3100 | MPa | |
| 150°C | 2800 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Yield, 60°C | 85.0 | MPa | |
| Yield, 90°C | 70.0 | MPa | |
| Yield, 120°C | 55.0 | MPa | |
| Yield, 150°C | 45.0 | MPa | |
| Break, 23°C | 120 | MPa | |
| Break, 60°C | 85.0 | MPa | |
| Break, 90°C | 65.0 | MPa | |
| Break, 120°C | 55.0 | MPa | |
| Break, 150°C | 45.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Yield, 60°C | 4.0 | % | |
| Yield, 90°C | 6.0 | % | |
| Yield, 120°C | 6.0 | % | |
| Yield, 150°C | 6.0 | % | |
| Break, 23°C | 3.5 | % | |
| Break, 60°C | 5.0 | % | |
| Break, 90°C | 6.0 | % | |
| Break, 120°C | 7.0 | % | |
| Break, 150°C | 7.0 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 10 | kJ/m² | |
| 23°C | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 75 | kJ/m² | |
| 23°C | 65 | kJ/m² | |
| Notched Izod Impact | ASTM D256A | ||
| -20°C, 3.20 mm | 100 | J/m | |
| 23°C, 3.20 mm | 160 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 235 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 100 | °C | |
| Vicat Softening Temperature | 245 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 260 to 290 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 MPa of cavity pressure |
| 2 . | 20,000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Salflex 520TM | Salflex Polymers Ltd. | HDPE | Salflex |
| RheTech Polypropylene G20P252-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Sindustris PP HI5205 | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| TEREZ PBT TM 4250 | TER HELL PLASTIC GMBH | PBT | TEREZ PBT |
| Colorite 77 Series 7777 | Colorite Polymers | PVC, Unspecified | Colorite 77 Series |