EnCom S PC 1614 R
| Category: | PC , Polycarbonate |
| Manufacturer: | EnCom, Inc. |
| Trademark: | EnCom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hm5iWN_EnCom-S-PC-1614-R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low Coef. of Friction, Injection Molding Grade |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 17 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 113 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 63.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 120 | % | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 800 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 129 | °C | |
| 1.8 MPa, Unannealed | 124 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.18 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 to 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 to 75 | % | |
| Rear Temperature | 271 to 293 | °C | |
| Middle Temperature | 282 to 304 | °C | |
| Front Temperature | 288 to 316 | °C | |
| Nozzle Temperature | 288 to 310 | °C | |
| Processing (Melt) Temp | 293 to 316 | °C | |
| Mold Temperature | 71.1 to 98.9 | °C | |
| Back Pressure | 0.345 to 0.689 | MPa | |
| Screw Speed | 30 to 70 | rpm | |
| Vent Depth | 0.038 to 0.076 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Miramid® H3KC | BASF Leuna GmbH | Nylon 6 | Miramid® |
| VESTAMID® HTplus M1900 | Evonik Industries AG | PPA | VESTAMID® HTplus |
| XYRON™ L574Z | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| HANWHA CTBA-8730BK | Hanwha Chemical | Polyolefin, Unspecified | HANWHA |
| ICORENE® 1901 | ICO Polymers EMEA, A Division of A. Schulman | Plastomer | ICORENE® |