VENYL UW500
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hlvBis_VENYL-UW500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UW500 is a 50% glass bead filled polyamide 66 intended for Injection moulding. APPLICATIONS VENYL UW500 has been developed especially for very demanding applications in automotive industry and electrical parts. VENYL UW500 is available in black (VENYL UW500 - 8229) but other colours can be provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.56 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.60 to 1.0 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.2 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 17 | % | ISO 527-2 |
| Flexural Modulus | 5700 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 34 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 255 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 215 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | °C | ISO 3146 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 650 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 285 to 300 | °C | |
| Middle Temperature | 280 to 295 | °C | |
| Front Temperature | 275 to 290 | °C | |
| Nozzle Temperature | 265 to 280 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Injection Pressure | 85.0 to 110 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Technacet® B-110 | Poly Plastic | Acetal (POM) Homopolymer | Technacet® |
| WPP PP PPHFGC-1 | Washington Penn Plastic Co. Inc. | PP Homopolymer | WPP PP |
| XYRON™ L564V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| EUROPLEX® Film HC 99716 | Evonik Industries AG | PVDF+PMMA | EUROPLEX® Film |
| LUVOCOM® 1105-9193/BL | LEHVOSS Group | PEEK | LUVOCOM® |