Generic SAN
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hlTmho_Generic-SAN.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic SAN This information is provided for comparative purposes only. |
| General Information |
|---|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.04 - 1.08 | g/cm³ | ASTM D792 |
| 23°C | 1.06 - 1.08 | g/cm³ | ISO 1183 |
| Apparent Density | 0.65 - 0.69 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/3.8 kg | 4.3 - 26 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 2.6 - 100 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 9.65 - 56.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow : 23°C | 0.35 - 0.51 | % | ASTM D955 |
| 23°C | 0.35 - 0.50 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.29 - 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| 23°C | 83 - 125 | ASTM D785 | |
| 23°C | 81 - 86 | ISO 2039-2 | |
| Ball Indentation Hardness | 155 - 175 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 23°C | 3100 - 3710 | MPa | ASTM D638 |
| 23°C | 3460 - 4730 | MPa | ISO 527-2 |
| Tensile Strength | |||
| Yield, 23°C | 63.6 - 80.4 | MPa | ASTM D638 |
| Yield, 23°C | 52.0 - 89.4 | MPa | ISO 527-2 |
| Fracture, 23°C | 67.5 - 72.8 | MPa | ASTM D638 |
| Fracture, 23°C | 52.0 - 75.3 | MPa | ISO 527-2 |
| 23°C | 60.8 - 96.5 | MPa | ASTM D638 |
| Tensile Elongation | |||
| Yield, 23°C | 2.5 - 4.1 | % | ASTM D638 |
| Fracture, 23°C | 1.7 - 6.7 | % | ASTM D638 |
| Fracture, 23°C | 1.9 - 7.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| 23°C | 3040 - 3790 | MPa | ASTM D790 |
| 23°C | 2600 - 3880 | MPa | ISO 178 |
| Flexural Strength | |||
| 23°C | 87.0 - 120 | MPa | ASTM D790 |
| 23°C | 86.0 - 132 | MPa | ISO 178 |
| Yield, 23°C | 88.1 - 124 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 1.5 - 3.1 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength (23°C) | 11 - 21 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 9.8 - 30 | J/m | ASTM D256 |
| 23°C | 1.5 - 3.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact | |||
| 23°C | 17 - 370 | J/m | ASTM D256 |
| 23°C | 12 - 20 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 94.8 - 99.1 | °C | ASTM D648 |
| 0.45 MPa, not annealed | 82.0 - 103 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 80.8 - 97.4 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 84.8 - 101 | °C | ISO 75-2/A |
| 1.8 MPa, annealed | 97.0 - 103 | °C | ASTM D648 |
| 1.8 MPa, annealed | 86.0 - 102 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 93.8 - 110 | °C | ASTM D1525 |
| -- | 99.0 - 110 | °C | ISO 306 |
| CLTE - Flow | |||
| -- | 5.9E-5 - 6.9E-5 | cm/cm/°C | ASTM D696 |
| -- | 5.0E-5 - 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dissipation Factor (23°C) | 1.0E-4 - 8.0E-3 | IEC 60250 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 86.2 - 89.3 | % | ASTM D1003 |
| Haze | 0.40 - 2.8 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 73.9 - 85.0 | °C | |
| Drying Time | 1.9 - 4.0 | hr | |
| Suggested Max Moisture | 0.010 - 0.20 | % | |
| Suggested Shot Size | 58 - 60 | % | |
| Rear Temperature | 170 - 232 | °C | |
| Middle Temperature | 190 - 232 | °C | |
| Front Temperature | 198 - 231 | °C | |
| Nozzle Temperature | 205 - 231 | °C | |
| Processing (Melt) Temp | 204 - 250 | °C | |
| Mold Temperature | 49.0 - 70.3 | °C | |
| Injection Pressure | 4.00 - 126 | MPa | |
| Back Pressure | 0.0862 - 44.1 | MPa | |
| Screw Speed | 45 - 80 | rpm | |
| Clamp Tonnage | 3.4 - 4.8 | kN/cm² |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic SANThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SEPAZ™ 220A | Mando Advanced Materials Co., Ltd. | PPA | SEPAZ™ |
| VITAMIDE® BK70BK6683 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Witcom PP 2008/003 | Witcom Engineering Plastics B.V. | PP, Unspecified | Witcom PP |
| Mytex® AX521HX-02 | Mytex Polymers | PP, Unspecified | Mytex® |
| LUBMER™ L4620 | Mitsui Chemicals America, Inc. | HMWPE | LUBMER™ |