NAXELL™ PC429HHI
| Category: | PC , Polycarbonate |
| Manufacturer: | MRC Polymers, Inc. |
| Trademark: | NAXELL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hkTWST_NAXELL-PC429HHI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PC429HHI is available in natural and custom colors, internal and external lubricants, UV stabilized and other modifications. Further information and details are available upon request . |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 55.0 | MPa | ASTM D638 |
| Flexural Modulus - Secant | 2070 | MPa | ASTM D790 |
| Flexural Strength | 86.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 640 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -29°C | 60.0 | J | |
| 23°C | 56.0 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 124 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 114 | °C | |
| CLTE - Flow (-40 to 35°C) | 6.5E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2099 X 115382 C | RTP Company | PLA+HDPE | RTP |
| SABIC® Vestolen A 6060R b | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® Vestolen A |
| Durethan® BKV 30 H2.0 EF DUS029 901510 | LANXESS Corporation | Nylon 6 | Durethan® |
| LUVOCOM® 1115-8559 | Lehmann & Voss & Co. | PEKK | LUVOCOM® |
| Elastocon® 2840B | Elastocon TPE Technologies | TPE | Elastocon® |