ASTALOY™ ABS/PET MDA257
| Category: | ABS+PET , Acrylonitrile Butadiene Styrene + PET |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTALOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hkEUre_ASTALOY-ABS-PET-MDA257.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTALOY™ MDA257 is an alloy of ABS and 100% recycled polyethylene terephthalate (PET). Note: The letters "U" or "W" indicate UV stabilisation has been added [ ie: ASTALOY™ MDA257-U ]. ASTALOY™ MDA257 is a development grade, the typical values detailed on this data sheet are based on limited data and are subject to frequent review |
| General Information | |
|---|---|
| Recycled Content |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.12 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 9.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow 1(3.00 mm) | 0.60 - 1.0 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.25 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 98 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2(3.20 mm) | 39.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 45 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2000 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 3.20 mm | 150 | J/m | ASTM D256 |
| -20°C, 3.20 mm | 60 | J/m | ASTM D256 |
| Dart Drop Impact (3.20 mm) | 50.0 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 3.20mm | 70.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 76.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 12.7mm | 83.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 112 | °C | ASTM D1525 6 |
| CLTE - Flow | 6.9E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Additional Information |
|---|
| Glow Wire Temperature, AS 2420, 1.6 mm: 550°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 - 120 | °C | |
| Drying Time | 3.0 - 5.0 | hr | |
| Rear Temperature | 215 - 235 | °C | |
| Middle Temperature | 225 - 245 | °C | |
| Front Temperature | 235 - 255 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 50.0 - 90.0 | °C | |
| Injection Pressure | 60.0 - 140 | MPa | |
| Injection Rate | Moderate | ||
| Back Pressure | 0.100 - 0.500 | MPa | |
| Screw Speed | 40 - 60 | rpm | |
| Clamp Tonnage | 3.0 - 6.0 | kN/cm² |
| Injection instructions |
|---|
| Nozzle Temperature: Do not exceed stock temperature |
| Note Message | |
|---|---|
| 1 . | D2 type |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2740 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| 4MID® 9B30000 | 4Plas | Nylon 6 | 4MID® |
| KumhoSunny PBT 3710FG-NH | Shanghai KumhoSunny Plastics Co., Ltd. | PBT | KumhoSunny PBT |
| Karina CLEAR PVC COMPOUND -E 75/236-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® PPH-2.6-BOPP | Osterman & Company | PP Homopolymer | Osterlene® |