Durethan® BKV 50 H EF DUS022 900116
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hh8I97_Durethan-BKV-50-H-EF-DUS022-900116.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 50 % glass fibers, injection molding, improved flowability, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.57 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.70 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.070 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.20 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.020 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 16200 | 9500 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 205 | 128 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 2.3 | 4.3 | % | ISO 527-2/5 |
| Flexural Modulus 5(23°C) | 15000 | 9700 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | -- | 197 | MPa | |
| 23°C 6 | 320 | 203 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 2.9 | 4.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6, GHR, 10-160, GF50 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | -- | kJ/m² | |
| 23°C | 13 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 85 | 80 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 11 | -- | kJ/m² | |
| 23°C | 14 | 20 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 75 | -- | kJ/m² | |
| 23°C | 80 | 70 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy (23°C) | 3.60 | 5.80 | J | ISO 6603-2 |
| Multi-Axial Instrumented Impact Peak Force (23°C) | 1220 | 1260 | N | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 215 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 207 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 1.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 80.0 to 120 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 227 A FR | RTP Company | Nylon 6 | RTP |
| Prime Impax 250 | Primex Plastics Corporation | PS (HIPS) | Prime Impax |
| AvaSpire® AV-848 GF30 | Solvay Specialty Polymers | PAEK | AvaSpire® |
| ESTACARB 1060 V0 HF | Cossa Polimeri S.r.l. | PC | ESTACARB |
| LNP™ THERMOCOMP™ DF0049P compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |