PRL PC/ABS-FR1
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hgs7FE_PRL-PC-ABS-FR1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL PC/ABS-FR1 is a Polycarbonate + ABS (PC+ABS) product. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/5.0 kg) | 25 to 50 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 62.1 | MPa | |
| Break, 3.18 mm | 56.5 | MPa | |
| Flexural Modulus (3.18 mm) | 2620 | MPa | ASTM D790 |
| Flexural Strength (3.18 mm) | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 640 | J/m | ASTM D256 |
| Gardner Impact (3.18 mm) | 36.2 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 90.6 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 85.0 | °C | |
| RTI Elec | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 2.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Imp | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 2.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C | |
| RTI Str | UL 746 | ||
| 1.50 mm | 60.0 | °C | |
| 2.50 mm | 60.0 | °C | |
| 3.00 mm | 60.0 | °C |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Comparative Tracking Index (CTI) (1.50 mm) | PLC 0 | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | ||
| 1.50 mm | PLC 0 | ||
| 2.50 mm | PLC 0 | ||
| 3.00 mm | PLC 0 | ||
| Hot-wire Ignition (HWI) | UL 746 | ||
| 1.50 mm | PLC 3 | ||
| 2.50 mm | PLC 3 | ||
| 3.00 mm | PLC 1 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 5VA |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 to 82.2 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 221 to 254 | °C | |
| Middle Temperature | 232 to 266 | °C | |
| Front Temperature | 243 to 277 | °C | |
| Processing (Melt) Temp | 246 to 274 | °C | |
| Mold Temperature | 48.9 to 82.2 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen H30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Xuchuan XCB-30 | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Cellophane™ 390MSC | Innovia Films Ltd. | Cellulose, Regenerated | Cellophane™ |
| Sylvin 9940-60 NATURAL | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Durethan® AKV 35 H2.0 SR1 901510 | LANXESS Corporation | Nylon 66 | Durethan® |