LNP™ LUBRICOMP™ WFL36 compound
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hgmthv_LNPLUBRICOMPWFL36compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* WFL36 is a compound based on Polybutylene Terephalate resin containing Glass Fiber, PTFE. Added features of this material include: Internally Lubricated. Also known as: LNP* LUBRICOMP* Compound WFL-4036 Product reorder name: WFL36 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.10 - 0.30 | % | ASTM D955 |
| Transverse flow : 24 hours | 0.50 - 1.0 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 0.50 - 1.0 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.10 - 0.30 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10300 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength (Break) | 118 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation | |||
| Fracture | 2.3 | % | ASTM D638 |
| Fracture | 2.2 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 10200 | MPa | ASTM D790 |
| -- | 10000 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 187 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.57 | ASTM D3702 Modified | |
| With Self-Static | 0.41 | ASTM D3702 Modified | |
| Wear Factor - Washer | 42.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 96 | J/m | ASTM D256 |
| 23°C 2 | 9.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 680 | J/m | ASTM D4812 |
| 23°C 3 | 43 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 13.7 | J | ASTM D3763 |
| -- | 2.61 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 218 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 4 | 214 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 - 232 | °C | |
| Middle Temperature | 243 - 254 | °C | |
| Front Temperature | 260 - 271 | °C | |
| Processing (Melt) Temp | 238 - 266 | °C | |
| Mold Temperature | 82.2 - 98.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 303 HF EM | RTP Company | PC | RTP |
| Toyolac® 824V X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Addisil™ 60 Xray | Momentive Performance Materials Inc. | Rubber | Addisil™ |
| Ducor® DE3240N | Ducor Petrochemicals BV | PP Random Copolymer | Ducor® |
| PENTAMID B MK30 H schwarz | PENTAC Polymer GmbH | Nylon 6 | PENTAMID B |