BMC 605LWR
| Category: | Polyester, TS , Thermoset Polyester |
| Manufacturer: | Bulk Molding Compounds, Inc. |
| Trademark: | BMC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hcXdbD_BMC-605LWR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| BMC 605LWR is a mineral filled, glass fiber reinforced polyester bulk molding compound suitable for compression, transfer and stuffer injection molding. It is designed to provide improved wear resistance compared to standard BMC605. BMC 605LWR is produced in extruded form in a range of industrial colors. It is available in logs up to 12 inches in length or as precut slugs of specific weight, in diameters 1" to 2 ½" . Within this range, smaller diameters are supplied as multiple extrusions and weight tolerances are plus or minus 5 %, up to a maximum of plus or minus 15 grams. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.87 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (Compression Molded) | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.10 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 18 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, Compression Molded) | 37.9 | MPa | ASTM D638 |
| Flexural Strength (Compression Molded) | 96.5 | MPa | ASTM D790 |
| Compressive Strength | 128 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 210 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 260 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | 12 | kV/mm | ASTM D149 |
| Arc Resistance | 180 | sec | ASTM D495 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.59 mm | V-0 | ||
| 3.18 mm | V-0 | ||
| 6.35 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Mold Temperature | 138 to 166 | °C |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2950-80 White 1437 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Sylvin 9658-45 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ACRYPET® IR H30 | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | ACRYPET® |
| Franprene TGA 2345LMO | Franplast S.r.l. | TPE | Franprene |
| LUVOCOM® 1-1129 | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |