Microthene® G MU76300
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Microthene® G |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hbf5H6_Microthene-G-MU76300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Microthene G polyolefin powders are ground, irregularly-shaped particles for use in a broad range of specialty applications. Microthene G powders combine the unique properties of a polyolefin resin with a small ground particle size. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 10 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 9.0 | wt% | |
| Average Particle Size | 35 | mesh | Internal Method |
| Particle Shape | Irregular |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore D | 47 | ||
| Shore D, 15 sec | 42 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 12.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 760 | % | ASTM D638 |
| Flexural Modulus | 144 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 72.0 | °C | ASTM D1525 |
| Melting Temperature | 95.1 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 5702P | SABIC Americas, Inc. | PP Homopolymer | SABIC® PP |
| SLOVAMID® 6 GF 15 LS | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Foam-It® 10 SLOW | Smooth-On, Inc | PUR, Unspecified | Foam-It® |
| HiFill® PA6 GF20 L UV | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| Jam PE 41X01 | Jam Petrochemical Company | HDPE | Jam PE |