HONES® PA66 GF10
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Guangdong Shunde Hones Polymer Material Co., Ltd. |
| Trademark: | HONES® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | hbEtM0_HONES-PA66-GF10.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Technology characteristics: 10% Glass fiber reinforced, flame retardant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 90.0 | MPa | ASTM D638 |
| Flexural Strength | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 10 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 45 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 190 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | 26 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.00 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.20 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 220 to 265 | °C | |
| Middle Temperature | 260 to 270 | °C | |
| Front Temperature | 260 to 270 | °C | |
| Nozzle Temperature | 260 to 270 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech C706 | Shanghai Suptech Engineering Plastics Co. Ltd. | PC | Sup-tech |
| Valtra® EA3300 | Saudi Polymers Company | PS (GPPS) | Valtra® |
| Kelon® A H CEG/40 | LATI S.p.A. | Nylon 66 | Kelon® A |
| I. Stern IS-7985 | I. STERN & CO. INC. | PET | I. Stern |
| Hostacom M2 T02 102942 | LyondellBasell Industries | PP Homopolymer | Hostacom |